PENGARUH AKTIVASI DENGAN NaOH TERHADAP PERFORMANCE TiO2/C BERPENDUKUNG KERAMIK SEBAGAI ELEKTRODA SUPERKAPASITOR

Hanif, Wahyuni (2016) PENGARUH AKTIVASI DENGAN NaOH TERHADAP PERFORMANCE TiO2/C BERPENDUKUNG KERAMIK SEBAGAI ELEKTRODA SUPERKAPASITOR. Diploma thesis, Universitas Andalas.

[img]
Preview
Text (abstrak)
a. Abstrak.pdf - Published Version

Download (112kB) | Preview
[img]
Preview
Text (BAB 1)
b. BAB 1.pdf - Published Version

Download (120kB) | Preview
[img]
Preview
Text (BAB Akhir)
c. BAB Akhir.pdf - Published Version

Download (111kB) | Preview
[img]
Preview
Text (Daftar pustaka)
d. Daftar Pustaka.pdf - Published Version

Download (228kB) | Preview
[img] Text (Skripsi full text)
e. Karya Ilmiah utuh.pdf - Published Version
Restricted to Repository staff only

Download (1MB)

Abstract

Effect of activated by NaOH on the performance of TiO2/C reinforced ceramics as electrode of supercapacitor have been done. Synthesis of TiO2 sol was used sol-gel method. Membrane of ceramic as template TiO2/C growth that activated by NaOH was prepared as electrode of supercapacitor which used polymer hydrogel electrolyte, polyvinyl alcohol as separator and phosphoric acid (H3PO4) as electrolyte. Effect activated by NaOH at the electrode of supercapacitor can increase the capacitance at temperature calcined 250oC and 300oC. Based on characterization of EDX (Energy Dispersive X-Ray), the most high contain of carbon was electrode after activated at temperature calcined 300oC was 60,67%, which is the higest capacitance was 14540 nF with concentration of electrolyte H3PO40,5 M, voltase 0,62 volt and current 5,3 µA at charger time 30 minutes with conductivity 45,4x10-5 S/cm.

Item Type: Thesis (Diploma)
Subjects: Q Science > QD Chemistry
Divisions: Fakultas Matematika dan Ilmu Pengetahuan Alam > Kimia
Depositing User: s1 kimia kimia
Date Deposited: 31 Aug 2016 07:17
Last Modified: 31 Aug 2016 07:17
URI: http://scholar.unand.ac.id/id/eprint/16230

Actions (login required)

View Item View Item