PENGARUH WAKTU ULTRASONIKASI TERHADAP SIFAT MEKANIK FILM NANOSELULOSA SERAT PINANG

AL, RAHMAN (2020) PENGARUH WAKTU ULTRASONIKASI TERHADAP SIFAT MEKANIK FILM NANOSELULOSA SERAT PINANG. Diploma thesis, UNIVERSITAS ANDALAS.

Preview	Text (COVER DAN ABSTRAK) COVER DAN ABSTRAK.pdf - Published Version Download (1MB) | Preview
Preview	Text (BAB 1) BAB 1 (PENDAHULUAN).pdf - Published Version Download (110kB) | Preview
Preview	Text (BAB 5) BAB AKHIR (KESIMPULAN).pdf - Published Version Download (100kB) | Preview
Preview	Text (DAFTAR PUSTAKA) DAFTAR PUSTAKA.pdf - Published Version Download (112kB) | Preview
	Text (FULL TEXT) TUGAS AKHIR ILMIAH UTUH.pdf - Published Version Restricted to Repository staff only Download (2MB)

Abstract

Telah dilakukan penelitian mengenai pengaruh waktu ultrasonikasi terhadap sifat mekanik nanoselulosa serat pinang. Variasi waktu 30, 60, 90, 120 menit. Perlakuan Alkalisasi NaOH yaitu 18%. Karakterisasi fasa dan ukuran kristal selulosa menggunakan XRD (X- Ray Diffractometer). Karakterisasi morfologi dan ukuran partikel selulosa menggunakan SEM (Scanning Electron Microscopy). Karakterisasi transparansi selulosa menggunakan Spectrometer Visible. Sifat mekanik yang diujikan meliputi kuat tarik, regangan, modulus elastisitas. Dari hasil pengujian didapatkan ukuran kristal dan indek kristalinitas diperoleh yaitu 39,77 nm dan 61,89 %. Nilai absorpsi minimum dan trasmitansi maksimum yaitu 7,68 % dan 17,6 %. Uji kekuatan sifat mekanik menghasilkan kekuatan tarik dan modulus elastisitas tertinggi dari serat pinang diperoleh pada waktu ultrasonikasi 30 menit 0,98 MPa, dan 1,6 MPa. Nilai regangan tertinggi pada waktu 60 menit yaitu 6,2%. Berdasarkan hasil karakterisasi, Perlakuan setelah alkalisasi NaOH dan setelah bleaching dihasilkan tingkat indek kristalinitas yang tinggi.