PENGARUH KONSENTRASI PREKURSOR ZINC NITRATE TETRAHYDRATE (ZN(NO3)2.4H2O) DAN HEXAMETHLENETETRAMINE (C6H12N4) TERHADAP GEOMETRI DAN UKURAN NANOPARTIKEL SENG OKSIDA

Fitria, Ardhiati (2019) PENGARUH KONSENTRASI PREKURSOR ZINC NITRATE TETRAHYDRATE (ZN(NO3)2.4H2O) DAN HEXAMETHLENETETRAMINE (C6H12N4) TERHADAP GEOMETRI DAN UKURAN NANOPARTIKEL SENG OKSIDA. Diploma thesis, Universitas Andalas.

Preview	Text (Cover dan Abstrak) 1. Cover dan Abstrak.pdf - Published Version Download (89kB) | Preview
Preview	Text (BAB I Pendahuluan) 2. BAB I Pendahuluan.pdf - Published Version Download (45kB) | Preview
Preview	Text (BAB V Kesimpulan dan Saran) 3. BAB V Kesimpulan dan Saran.pdf - Published Version Download (33kB) | Preview
Preview	Text (Daftar Pustaka) 4. Daftar Pustaka.pdf - Published Version Download (39kB) | Preview
	Text (Skripsi full text) 5. Skripsi fulltext.pdf - Published Version Restricted to Repository staff only Download (3MB)

Abstract

Nanopartikel ZnO disintesis menggunakan metode hidrotermal. Larutan ZnO dengan konsentrasi 15, 20, 25, 30, dan 35 mM disiapkan menggunak prekursor zinc nitrate tetrahydrate dan hexamethylenetetramine. Prekursor tersebut dilarutkan dengan aquades dan diaduk sebelum proses hidrotermal berlangsung pada temperatur 95 °C selama 10 jam. Sampel ZnO dikarakterisasi menggunakan SEM dan XRD Hasil karakterisasi SEM menunjukkan bahwa nanopartikel ZnO yang terbentuk memiliki struktur nanorod dengan aspek rasio 1,1. Karakterisasi XRD menunjukkan bahwa sampel adalah ZnO dengan struktur kristal heksagonal. Ukuran kristal dihitung menggunakan persamaan Debye-Scherrer dan diperoleh bahwa ukuran kristal berada pada rentang 25,4 – 27,5 nm. Nanopartikel ZnO yang terbentuk berupa multi domain kristal yang terdiri atas tiga hingga empat domain dengan struktur kristal yang sama. Kata kunci: nanopartikel, konsentrasi prekursor, seng oksida (ZnO), hidrotermal