KARAKTERISASI SENSOR GAS HIDROGEN DARI BAHAN SEMIKONDUKTOR TITANIUM DIOXIDE (TIO2) DOPING SODIUM CARBONATE (NA2CO3)

Sri, Ramadhani (2018) KARAKTERISASI SENSOR GAS HIDROGEN DARI BAHAN SEMIKONDUKTOR TITANIUM DIOXIDE (TIO2) DOPING SODIUM CARBONATE (NA2CO3). Diploma thesis, Universitas Andalas.

Preview	Text (Cover dan Abstrak) Abstrak.pdf - Published Version Download (279kB) | Preview
Preview	Text (BAB I PENDAHULUAN) BAB I (PENDAHULUAN).pdf - Published Version Download (128kB) | Preview
Preview	Text (BAB AKHIR (PENUTUP)) BAB AKHIR(PENUTUP).pdf - Published Version Download (155kB) | Preview
Preview	Text (DAFTAR PUSTAKA) DAFTAR PUSTAKA.pdf - Published Version Download (129kB) | Preview
	Text (Tugas Akhir Ilmiah Utuh) Tugas Akhir Ilmiah Utuh.pdf - Published Version Restricted to Repository staff only Download (4MB)

Abstract

Telah dilakukan karakterisasi sensor gas hidrogen berupa pelet dari bahan semikonduktor TiO2-Na2CO3. Pelet sensor gas hidrogen dibuat sebanyak enam sampel dengan variasi komposisi yang berbeda. Tahap pembuatan sensor gas hidrogen terdiri atas pencampuran bahan, kalsinasi pada temperatur 500 oC selama 4 jam, penggerusan, kompaksi, dan sintering pada temperatur 700 oC selama 4 jam. Sensor gas hidrogen diuji pada temperatur ruang dengan melihat karakteristik I-V, nilai sensitivitas, nilai konduktivitas, waktu respon, dan karakterisasi XRD. Berdasarkan pengukuran karakteristik I-V sampel 98% mol TiO2 + 2% mol Na2CO3 memiliki sensitivitas tertinggi. Sensitivitas yang didapat yaitu 3,18 pada tegangan 6 volt. Nilai konduktivitas tertinggi dimiliki sampel 98% mol TiO2 + 2% mol Na2CO3 yaitu 1,30 x 10-3/Ωm pada lingkungan hidrogen. Waktu respon sampel 98% mol TiO2 + 2% mol Na2CO3 pada tegangan 6 volt adalah 57 sekon. Hasil XRD menunjukkaan ukuran kristal 98% mol TiO2 + 2% mol Na2CO3 lebih besar dibandingkan dengan TiO2 murni. Kata kunci: sensor gas hidrogen, TiO2-Na2CO3, sensitivitas, konduktivitas, waktu respon